Tork Metal | Steel shot

Click here to view the PDF file on this product.

Description

The Bainitic microstructure of steel is an ideal structure in cleaning of metal surfaces, other surface preparing processes and shot peening applications. Cool cracks and internal stresses in the structure is fragile as opposed containing non-resistant structure. Low carbon steel shots in the bainitic structure; a greater shock effect, higher impact effect, rapid rebound property, max. coating property, the loss of material has less wear properties.

Technical specs

GRAIN SIZES
Size	Particle Size (mm)
S 070	0,2 - 0,4
S 110	0,3 - 0,5
S 170	0,4 - 0,7
S 230	0,6 - 0,9
S 280	0,7 - 1,0
S 330	0,9 - 1,2
S 390	1,0 - 1,4
S 460	1,2 - 1,7
S 550	1,4 - 1,7
S 660	1,7 - 2,2
S 780	2,0 - 2,4
S 930	2,0 - 2,8
The grain size can be adjusted according to customer demands.

PACKAGING SPECIFICATIONS

25 Kg Package on pallets over 1 Tone

1 Tone in the Big Bags

TECHNICAL ANALYSIS
SYMBOL	CHEMICAL NAME	RATE
C	Carbon	0.10 – 0.15 %
Mn	Manganese	1.20 – 1.50 %
Si	Silicon	0.10 – 0.25 %
S	Sulfur	0.035 % max
P	Phosphor	0.035 % max

	TECHNICAL ANALYSIS	METHOD
Hardness	+/- 20 HRC (235HV)	ISO 11125-3
Hardness after Use	+/- 45 HRC (460HV)
Visible Density	App. 7,9 g/cm3	ISO 11125-4
Particle Shape	Maximum 15% shape defeat
Cavity	Max %15
Drawing Error	Max %5
Crack	Must not exist
Total Error	Max %20
Foreign Materials	It can be maximum 1%	ISO 11125-6
Humidity	Max %2 Max %2 Low Carbon corrosives should be stored in environments without humid. Otherwise, problems appear during using.	ISO 11125-7
Structure	As structure, bainitic and martensitic structure has been accepted as the standard.	ISO 11125-5
Chemical Composition	Carbon % 0.08-0.20 Manganese %0.35-1.50 Silicon % 0.10-2.00 Sulfur Max %0.05 Phosphorus Max %0.05	ISO 9556 ISO 629 ISO 439 ISO 4935 ISO 10714